| تكوين المواد: | كربيد التنجستن والكوبالت | مواصفات سبيكة: | YG8 ، YG6 ، YG6X ، YG9C ، YG11C ، YG13C |
|---|---|---|---|
| شكل: | أسطواني | الانتهاء من السطح: | لامع |
| لون: | سبيكة سوداء | نطاق الكثافة: | 12.33-15.0 جم/سم مكعب |
| نطاق الصلابة: | 86.5-93.6 HRA | نطاق TRS: | 1800-3800 ميجا باسكال |
| درجة المسامية: | A02/B00/C00 | حجم الحبوب: | 0.4-2.4 ميكرون |
| محتوى WC: | 69.2-94.0 ٪ | محتوى ني: | 6.0-16.0 ٪ |
| محتوى Ti: | 0-7.4 ٪ | محتوى TAC: | 0-13.8 ٪ |
| التخصيص: | متاح لكل رسم عميل أو عينة | ||
| إبراز: | YG8 YG6 YG6X YG9C YG11C YG13C Alloy Tungsten Carbide Seal Ring,High Temperature Resistance Tungsten Carbide Seal Ring,High Pressure Resistance Cemented Tungsten Carbide Sealing Ring,High Temperature Resistance Tungsten Carbide Seal Ring,High Pressure Resistance Cemented Tungsten Carbide Sealing Ring |
||
High temperature and high pressure resistant sealing ring designed for metallurgical equipment shafts.
| Grade | Composition(% in weight) | Physical Properties | Grain size(μm) | ||||||
|---|---|---|---|---|---|---|---|---|---|
| WC | Ni | Ti | TaC | A/B/C | Densityg/cm³(±0.1) | HardnessHRA(±0.5) | TRS Mpa(min) | Porosity | |
| KD115/YG6X | 93.5 | 6.0 | - | 0.5 | 14.90 | 93.0 | 2700 | A02/B00/C00 | 0.6-0.8 |
| KD335/YG10X | 89.0 | 10.5 | - | 0.5 | 14.40 | 91.8 | 3800 | A02/B00/C00 | 0.6-0.8 |
| KG6/YG6 | 94.0 | 6.0 | - | - | 14.90 | 90.5 | 2500 | A02/B00/C00 | 1.2-1.6 |
| KG8/YG8 | 92.0 | 8.0 | - | - | 14.75 | 90.0 | 3200 | A02/B00/C00 | 1.2-1.6 |
| KG9/YG9 | 91.0 | 9.0 | - | - | 14.60 | 89.0 | 3200 | A02/B00/C00 | 1.2-1.6 |
| KG9C/YG9C | 91.0 | 9.0 | - | - | 14.60 | 88.0 | 3200 | A02/B00/C00 | 1.6-2.4 |
| KG10/KG10 | 90.0 | 10.0 | - | - | 14.50 | 88.5 | 3200 | A02/B00/C00 | 1.2-1.6 |
| KG11/YG11 | 89.0 | 11.0 | - | - | 14.35 | 89.0 | 3200 | A02/B00/C00 | 1.2-1.6 |
| KG11C/YG11C | 89.0 | 11.0 | - | - | 14.40 | 87.5 | 3000 | A02/B00/C00 | 1.6-2.4 |
| KG13/YG13 | 87.0 | 13.0 | - | - | 14.20 | 88.7 | 3500 | A02/B00/C00 | 1.2-1.6 |
| KG13C/YG13C | 87.0 | 13.0 | - | - | 14.20 | 87.0 | 3500 | A02/B00/C00 | 1.6-2.4 |
| KG15/YG15 | 85.0 | 15.0 | - | - | 14.10 | 87.5 | 3500 | A02/B00/C00 | 1.2-1.6 |
| KG15C/YG15C | 85.0 | 15.0 | - | - | 14.00 | 86.5 | 3500 | A02/B00/C00 | 1.6-2.4 |
| KD118/YG8X | 91.5 | 8.5 | - | - | 14.50 | 93.6 | 3800 | A02/B00/C00 | 0.4-0.6 |
| KD338/YG12X | 88.0 | 12.0 | - | - | 14.10 | 92.8 | 2200 | A02/B00/C00 | 0.4-0.6 |
| KD25/P25 | 77.4 | 8.5 | 6.5 | 6.0 | 12.60 | 91.8 | 2200 | A02/B00/C00 | 1.0-1.6 |
| KD35/P35 | 69.2 | 10.5 | 5.2 | 13.8 | 12.70 | 91.1 | 2500 | A02/B00/C00 | 1.0-1.6 |
| KD10/M10 | 83.4 | 7.0 | 4.5 | 4.0 | 13.25 | 93.0 | 2000 | A02/B00/C00 | 0.8-1.2 |
| KD20/M20 | 79.0 | 8.0 | 7.4 | 3.8 | 12.33 | 92.1 | 2200 | A02/B00/C00 | 0.8-1.2 |
| Grade | Composition (% in weight) | Physical Properties | Equivalent domestic | ||||||
|---|---|---|---|---|---|---|---|---|---|
| WC | Ni | Ti | Density g/cm³ (±0.1) | Hardness HRA (±0.5) | TRS Mpa (min) | Porosity ABC | Grain size (μm) | ||
| KDN6 | 93.8 | 6.0 | 0.2 | 14.6-15.0 | 89.5-90.5 | 1800 | A02B00C00 | 0.8-2.0 | YN6 |
In our journey at Kedel Technology Co., Ltd. in Chengdu, every encounter with you is our honor. We are well aware that being able to stop here among the many choices is our greatest support and recognition. Your satisfaction is our relentless pursuit, and every positive review and repurchase is the driving force that inspires us to keep moving forward.